Silica Mortar, Refractory Mortar, Mortar manufacturer / supplier in China, offering Refactory Silica Mortar for Coke Oven, Refractory Aluminate Cement on Sale, Calcium Aluminate Cement A70 in Refractory and so on.

(/ )

Supplier Homepage Product refractory brick refractory for coke oven Refactory Silica Mortar for Coke Oven

Refactory Silica Mortar for Coke Oven

FOB Price: US $200-700 / Ton
Min. Order: 1 Ton
Min. Order FOB Price
1 Ton US $200-700/ Ton
Get Latest Price
Production Capacity: 5000tons
Transport Package: Be Packed in Moisture Bag
Payment Terms: L/C, T/T, Western Union

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: KH-sm
  • Feature: Long Time Materials
  • Shape: Powder
  • Quality: Excellent
  • MOQ: Negotiable
  • Specification: ISO, GB
  • HS Code: 2508700010
  • Refractoriness (℃): 1580< Refractoriness< 1770
  • Type: Refractory Material
  • Material: Silica & Clay
  • Price: Competitive
  • Trademark: KH
  • Origin: Zhengzhou
Product Description

Refractroy Silica Mortar:

Descriptions: silica mortar is mainly used for masonry of high quality silica bricks. Packed with paper bag outside, there is plastic moisture proof bag inside. Weight per bag is 25kg and there is one small bag of additives in each bag of mortar. The red sign on the front of the package is obvious, which is used to distinguish it from other bulk material during application.

Mixing sequence: the silica mortar is the fine powder (0.088mm). Put the mortar in to the mixer and spray the small bag of additives on the dry powder evenly, mix them for 3 to 5min. Next, put 32 to 35 per cent of clean water (tap water and water amount can be adjusted according to actual conditions) into it and continue mixing for 5 to 10min. The effect will be better if you put the mortar slurry static for 10min. Amount of agitation should be determined according to the capacity of mixer. But it must be used by the bag.

The mortar well mixed should be used as soon as possible for fear of loosing effectiveness.

Precautions: it is prohibited to put the additives into the water separately; it is prohibited to use acid industrial waste water to mix the slurry; operate strictly according to the requirements, or else it will influence the masonry quality and useful life of the mortar.


1.High binding strength, good structural integrity
2.High softening temperature under loading, low shrinkage at high temperature
3.Small gap and little gas, easy for mixing and construction 
4.Stable properties, good resistance to erosion
5.Excellent Plasticity ,long service life


1.Mainly used for silica bricks masonry.
2.Used in various industrial kilns, blast furnace and hot stove.
3.Used in the lining of industrial furnaces.

Technical Data:


SiO2,% ≥92859496949494
Fe2O3,% ≥
Al2O3,% ≤2.52.810.70.8

Cohering Times80-12080-12080-12080-12060-12060-12060-120
Breaking Strength,Mpa(110C drying) ≥1110.
Breaking Strength,Mpa(140C*3h) ≥3330.521.51.5
Refractoriness Under Load,C ≥15001420160016201600

Refactory Silica Mortar for Coke Oven
Refactory Silica Mortar for Coke Oven




Send your message to this supplier
Miss Anna Lee
Project Manager
To: Miss Anna Lee

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category